Ornamental member

ABSTRACT

An improved ornamental member including at least two types of Cr or Ti hard films of different color tones disposed by ion plating on a substrate is prepared. The laminate includes a combination of Cr and Ti hard films including a stainless steel colored Cr hard film layer containng Cr, N and C as the main constituents, a gold colored Ti hard film having Ti and N as the main constitutents, a dark grey Ti hard film having Ti, N and C as the main constituents, a blue Ti hard film having Ti and O as the main constituents and a brown Ti hard film having Ti, O and C as the main constituents. The thickness of a single year of hard film is between about 0.2 and 1.5 μm and the total film thickness at the laminated portion is less than about 3 μm. Preferably, each hard film layer is between about 0.2 and 0.8 μm.

BACKGROUND OF THE INVENTION

This invention relates generally to an ornamental member produced by ion plating and more particularly to a multi-colored ornamental member formed of a combination of two hard films.

Conventional ornamental members, such as the exterior member of a watch with a multi-colored surface, include a stainless steel color and at least gold, dark grey, brown or blue. These generally are prepared by coating the surface of the ornamental member of a SUS material with a gold film produced by wet gold plating or ion plating, a dark grey film produced by wet rhodium or tin-nickel plating, or a brown film or a blue film produced by ion plating. A conventional exterior ornamental member of a watch with a two colored surface, including gold and brown or blue is generally produced by coating the surface of a substrate of the ornamental member with a gold film by gold or gold alloy wet plating and a brown or blue hard film produced by ion plating.

These conventional methods, however, suffer from poor scratch resistance, poor wear resistance and high cost. A partially exposed surface of a SUS material, which has a hardness of between about 140 and 180 Hv, is susceptible to scratching. A surface including a partial gold wet plated surface, which has a hardness of between about 200 and 300 Hv, is also susceptible to scratching. In order to enhance durability, it is necessary to increase the thickness of the layer of plating, which disadvantageously raises the cost of the article. A surface which is also partially wet plated with rhodium or tin-nickel is also susceptible to scratching. In addition, a rhodium plated surface is very expensive.

Accordingly, it is desirable to provide an improved ornamental member which eliminates these problems associated with the prior art and has good scratch resistance and wear resistance.

SUMMARY OF THE INVENTION

Generally speaking, in accordance with the invention, an improved ornamental member which has high ornamental value and hard surface has a substrate coated with a laminate of at least two hard films of Cr or Ti of different color tones by ion plating to form an ornamental member having a multi-colored surface. The laminate includes a combination of Cr and Ti hard films including a stainless steel colored Cr hard film layer containing Cr, N and C as the main constituents, a gold colored Ti hard film having Ti and N as the main constituents, a dark grey Ti hard film having Ti, N and C as the main constituents, a blue Ti hard film having Ti and 0 as the main constituents and a brown Ti hard film having Ti, 0 and C as the main constituents. The thickness of a single layer of the hard film is between about 0.2 and 1.5 μm and the total film thickness at the laminated portion is less than about 3 μm. Preferably, each hard film layer is between about 0.2 and 0.8 μm.

An ornamental member including one Cr hard film and one Ti hard film or two Ti hard film is formed by ion plating a first hard film on a substrate. A masking material is deposited in a pattern on the first hard film and a second hard film is ion plated on the first hard film and the masking material. The masking material is removed, removing the portion of the second hard film formed over it. Alternately, a first hard film is ion plated on the substrate and a second hard film is ion plated on the first hard film and the second hard film is partially removed by etching.

Accordingly, it is an object of this invention to provide an improved ornamental member having a multi-colored surface.

Another object of the invention is to provide an improved ornamental member having a high degree of hardness.

A further object of the invention is to provide an improved ornamental member with excellent scratch resistance, wear resistance and corrosion resistance.

A still further object of this invention is to provide an improved ornamental member with excellent adherence.

Yet a further object of this invention is to provide an improved ornamental member which is low in cost.

Still other objects and advantages of the invention will in part be obvious and will in part be apparent from the specification.

The invention accordingly comprises the several steps and the relation of one or more of such steps with respect to each of the others, and the article possessing the features, properties, and the relation of elements, which are exemplified in the following detailed disclosure, and the scope of the invention will be indicated in the claims.

BRIEF DESCRIPTION OF THE DRAWINGS

For a fuller understanding of the invention, reference is had to the following description taken in connection with the accompanying drawing, in which:

FIGS. 1(a), 1(b), 1(c) and 1(d) are sectional views illustrating the steps of preparing an ornamental member in accordance with an embodiment of the invention;

FIGS. 2(a), 2(b), 2(c) and 2(d) are sectional views illustrating the steps of preparing an ornamental member in accordance with another embodiment of the invention; and

FIGS. 3-21 are sectional views of an ornamental member in accordance with further embodiments of the invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

An ornamental member prepared in accordance with the invention is formed by a "second-layer ion plating method" or a "second-layer etching method". The ornamental member prepared by the second-layer ion plating method is shown in cross section in FIGS. 1(a)-1(d). A first hard film 2 is laminated on a substrate 1 by ion plating, as shown in FIG. 1(a). The laminate is baked and hardened. The portion of the surface of first hard film 2 intended to be visible is coated with an organic coating 3 to mask first hard film 2 as shown in FIG. 1(b).

A second hard film 4 is disposed across the upper surface by ion plating, as shown in FIG. 1(c). Substrate 1, including first hard film 2, inorganic coating 3 and second hard film 4, is immersed in an organic solvent to dissolve and remove inorganic coating 3 and the portion of second hard film 4 formed on inorganic coating 3. Thus, a two colored ornamental member including first hard film 2 and second hard film 4 is obtained as shown in FIG. 1(d).

Any material that can withstand the high temperature of ion plating may be used as substrate 1. For example, substrate 1 may be formed from a ceramic material, a hard Ni-base alloy, a Co-base alloy, stainless steel, a copper alloy, brass, zinc, a zinc alloy or a plastic material. Preferably, substrate 1 is SUS 304.

It is necessary for substrate 1 to have sufficient corrosion resistance prior to coating with the hard film since most of the hard films produced by ion plating include pinholes. If substrate 1 does not have sufficient corrosion resistance, it is necessary to form at least one undercoat layer by plating prior to ion plating first layer hard film 2. If substrate 1 is formed from a ceramic material, a hard Ni-base alloy, a Co-base alloy, stainless steel or the like, substrate 1 has good corrosion resistance and an undercoat plating is not necessary. However, if substrate 1 is a stainless steel substrate containing a free-cutting ingredient such as sulfur, substrate 1 is slightly inferior in corrosion resistance. In this case, it is necessary to laminate a single or several gold-, gold alloy-, chromium-, palladium-, palladium alloy-, rhodium- or ruthenium-plated layers as an undercoat to obtain a substrate with sufficient corrosion resistance.

If substrate 1 is a copper alloy, zinc or a zinc alloy, it is necessary to deposit a single or several gold-, gold alloy-, chromium-, palladium-, palladium alloy-, rhodium- or ruthenium-plated layers after laminating a single or several copper, Ni or Ni alloy layers on substrate 1. If an undercoat of a copper alloy, zinc or a zinc alloy is formed on substrate 1 prior to ion plating, it is possible to prevent the substrate material from being exposed directly to high temperature and a high vacuum atmosphere during ion plating. Thus, a rise in the internal temperature of the substrate material and the formation of a blister from the dezincification is prevented.

If substrate 1 is a plastic material, it is generally treated with Ni by electroless plating prior to undercoat plating in a manner similar to the undercoat plating of a copper alloy, zinc or a zinc alloy substrate. Since plastic is an organic material having a low melting point, gas easily escapes due to a rise in temperature during ion plating, causing frequent defective adhesion with the ion plated film. Thus, undercoat plating is essential to prevent defective adhesion.

The undercoat plating is between about 0.2 and 20 μm thick. In terms of productivity and functional efficiency, the undercoat is preferably between about 2 and 10 μm thick when the undercoat is formed of a single layer or is multi-layered. However, there is no difference is quality when the thickness is between about 0.2 and 20 μm thick.

First hard film 2 and second hard film 4 are formed of compounds including Cr or Ti. For example, a stainless steel colored hard film may be formed of a material including Cr, N and C. A gold coated hard film may be formed of a material including Ti and N. A dark grey hard film may be formed of a material including Ti, N and C, or Cr, N, C and 0. A blue hard film may be formed of a material including Ti and 0. A brown colored hard film may be formed of a compound including Ti, C and 0.

To form a two colored ornamental member in accordance with the invention, a combination of Cr and Ti hard films is used. For example, first hard film 2 may be a stainless steel colored Cr hard film and second hard film 4 may be a gold, dark grey, brown or blue colored Ti hard film. Alternatively, first hard film 2 may be a gold, dark grey, brown or blue colored Ti hard film and second hard film 4 may be a stainless steel colored Cr hard film.

It is also possible to form a two colored ornamental member from a combination of Ti hard films. For example, first hard film 2 may be formed of a gold colored Ti hard film and second hard film 4 may be formed of a blue or brown colored Ti hard film. Alternatively, first hard film 2 may be formed of a blue or brown colored Ti hard film and second hard film 4 may be formed of a gold colored Ti hard film.

An ornamental member including three or more colors in accordance with the invention is formed by combining Cr hard films and Ti hard films having different color tones.

Although an ion-plated film provides a high degree of hardness, an increase in the thickness of the hard film results in an increase in internal stress. Thus, the film becomes unfavorably brittle. To secure the adherence required for the ornamental member, the thickness of a single layer of hard film is between about 0.2 and 1.5 μm and the total film thickness of the laminated portion is less than about 3 μm. Preferably, a single layer hard film has a thickness between about 0.2 and 0.8 μm. If a single layer of hard film is less than about 0.2 μm, the scratch resistance and wear resistance are inferior and predetermined tones cannot be formed. If the thickness of the laminated portion exceeds about 3 μm, the internal stress lowers the adherence and the film may separate.

The method of forming an ornamental member in accordance with the invention by the second layer etching method is shown in FIGS. 2(a)-2(d). The second layer etching method may be used when one film is a Cr hard film and the other film is a Ti hard film. The second-layer ion plating method may be used when both films are Ti hard films or when one film is a Ti hard film and the other film is a Cr hard film.

First hard film 2 is formed on substrate 1 by ion plating, as shown in FIG. 2(a). A second hard film 5 is formed on first hard film 2 by ion plating, as shown in FIG. 2(b). The laminate is baked and hardened and an organic coating 6 is deposited on the surface portion of second hard film 5 where second hard film 5 is intended to be visible on the finished exterior, as shown in FIG. 2(c).

Substrate 1 including first hard film 2, second hard film 5 and organic coating 6 is immersed in a remover which dissolves only second hard film 5. Second hard film 5 is dissolved and removed except for the portions where second hard film 6 is covered with organic coating 6. Substrate 1 is immersed in an organic solvent to remove organic coating 6. Thus, a two colored ornamental member in accordance with the invention formed by a combination of first hard film 2 and second hard film 5 is obtained, as shown in FIG. 2(d).

As described above, an ornamental member in accordance with the invention includes at least two hard films of different color tones laminated on a substrate by ion plating to form an exterior surface including a multiplicity of colors. The hardness of the substrate of the ornamental member is not less than 1000 Hv over the entire surface. Thus, the scratch resistance and wear resistance are superior to those of a conventional ornamental member.

The following examples are set forth by way of illustration to show preparation of ornamental members in accordance with the invention. They are set forth for purposes of illustration only, and not intended in a limiting sense.

EXAMPLES

One hundred samples, in the shape of an exterior member of a watch, having two different colored hard films and the structures shown in FIGS. 3 through 14 were prepared. Examples 1 through 60 show coated ornamental members prepared in accordance with preferred embodiments of the invention. Comparative Examples 1 through 40 are set forth for purposes of comparison.

In each example, a first hard film was ion plated on the substrate in the following manner. A substrate formed of SUS 304, brass or zinc in the shape of an exterior member of a watch, was inserted into an evacuated ion plating device. Argon gas was introduced into the device and ion bombardment was carried out for five minutes with a negative voltage of 0.5 kV applied to the substrate while maintaining the pressure at 0.02 torr. Thus, the surface of substrate 1 was cleaned.

Argon gas was discharged and the pressure of the vacuum chamber was restored to 1×10⁻⁴ torr. Pure Ti or pure Cr was evaporated by electron beam heating, and a predetermined amount of a reaction gas was introduced to form a Ti or Cr hard film of an intermetallic compound of pure Ti or pure Cr and the reaction gas. The reaction gas was N₂ gas, C₂ H₂ gas and O₂ or gas mixtures including at least one of these gases. The thickness of the hard film was controlled by the evaporation time of pure Ti or pure Cr and the tone of the hard film was controlled by the kind of metal evaporated (Cr or Ti) and the reaction gas.

In the samples in which the ornamental member was prepared by the second layer ion plating method, the first hard film formed in the above-described manner, was coated with an inorganic coating Heat Resistant Masking Material-D produced by Okuno Seiyaku K.K. at the portions where the first hard film was intended to be visible as the exterior coating. The inorganic coating was dried in the manner shown in Table 13.

A second hard film of Ti or Cr was ion plated over the first hard film and the inorganic coating material in the same manner as the first hard film was ion plated over the substrate. The inorganic coating layer was dissolved by Trichlene ultrasonic cleaning. The portions of the second hard film covering the inorganic coating were removed upon dissolution of the inorganic coating material to form the samples of the ornamental member of Tables 1-12.

In the samples in which the ornamental member was formed by the second layer etching method, the first hard layer was formed in the above-described manner by the ion plating method. A second hard film of Ti or Cr was ion plated over the first hard film in the same manner as the first hard film was ion plated over the substrate.

SPR-557W, an organic coating material produced by Sanei Kagaku K.K., was deposited on the second hard film at the portions where the first hard film was intended to be visible a the exterior coating. The organic coating was dried in accordance with the procedures specified in Table 13. The portions of the second hard film not covered by the organic coating were removed in accordance with the procedure shown in Table 14. The organic coating was removed by Trichlene ultrasonic cleaning to form the samples of the ornamental member of Tables 1-12.

When brass and zinc were used as a substrate it was necessary to undercoat plate the substrate. The structure and the thickness of the undercoat plating of the Examples of the ornamental member in accordance with the invention and the Comparative Examples is shown in Table 15.

The conditions used to produce the samples of Examples 1-6 and Comparative Examples 1-4 having the structures shown in FIG. 3, and the results of evaluating the samples are shown in Table 1. Each sample included a stainless steel colored Cr first hard film 7 and a gold colored Ti second hard film 8 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 7-12 and Comparative Examples 5-8 having the structure shown in FIG. 4, and the results of evaluating the samples are shown in Table 2. Each sample included gold colored Ti first hard film 8 and stainless steel colored Cr second hard film 7 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 13-18 and Comparative Examples 9-12 having the structure shown in FIG. 5, and the results of evaluating the samples are shown in Table 3. Each sample included stainless steel colored Cr first hard film 7 and a dark grey colored Ti second hard film 9 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 19-24 and Comparative Examples 13-16 having the structure shown in FIG. 6, and the results of evaluating the samples are shown in Table 4. Each sample included dark grey colored Ti first hard film 9 and a stainless steel colored Cr second hard film 7 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 25-30 and Comparative Examples 17-20 having the structure shown in FIG. 7, and the results of evaluating the samples are shown in Table 5. Each sample included stainless steel colored Cr first hard film 7 and a brown colored Ti second hard film 10 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 31-36 and Comparative Examples 21-24 having the structure shown in FIG. 8, and the results of evaluating the samples are shown in Table 6. Each sample included brown colored Ti first hard film 10 and stainless steel colored Cr second hard film 7 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 36-42 and Comparative Examples 25-28 having the structure shown in FIG. 9, and the results of evaluating the samples are shown in Table 7. Each sample included a stainless steel colored Cr first hard film 7 and a blue colored Ti second hard film 11 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 43-48 and Comparative Examples 29-32 having the structure shown in FIG. 10, and the results of evaluating the samples are shown in Table 8. Each sample included blue colored Ti first hard film 11 and stainless steel colored Cr second hard film 7 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 49-51 and Comparative Examples 33-34 having the structure shown in FIG. 11, and the results of evaluating the samples are shown in Table 9. Each sample included gold colored Ti first hard film 8 and blue colored Ti second hard film 11 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 52-54 and Comparative Examples 35-36 having the structure shown in FIG. 12, and the results of evaluating the samples are shown in Table 10. Each sample included blue colored Ti first hard film 11 and a gold colored Ti second hard film 8 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 55-57 and Comparative Examples 37-38 having the structure shown in FIG. 13, and the results of evaluating the samples are shown in Table 11. Each sample included gold colored Ti first hard film 8 and brown colored Ti second hard film 10 disposed on substrate 1 of SUS 304, brass or zinc.

The conditions used to produce the samples of Examples 58-60 and Comparative Examples 58-60 having the structure shown in FIG. 14, and the results of evaluating the samples are shown in Table 12. Each sample included brown colored Ti first hard film 10 and gold colored Ti second hard film 8 disposed on substrate 1 of SUS 304, brass or zinc.

In Tables 1-12, "Processing time (min)" was the time required to deposit the metal of the evaporation source during ion plating. "Ratio" of gas is the ratio of the reaction gases used during ion plating. "Gas pressure" is the pressure in the vacuum tank in a stable state after the introduction of the reaction gases. Table 16 describes the criteria of properties evaluated in Tables 1-12.

                                      TABLE 1                                      __________________________________________________________________________               Example and  Invention               Comparison                                Comparative Example No.                                                                     1   2   3   4   5   6   1   2   3   4                   __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 2      FIG. 1  FIG. 2                            Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              SUS Brass                         material     304         304         304     304                               Undercoat    No  Yes Yes No  Yes Yes No  Yes No  Yes                           plating                                                              Hard film for first                                                                      Producing conditions                                                 layer     Evaporation  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1                           N.sub.2 :C.sub.2 H.sub.2                                                       Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1200                                                                               1400                                                                               1000                                                                               1200                                                                               1400                                                                               1000                                                                               1450                                                                               900 1450                                                                               900                           (HV)                                                                           Tone         SUS SUS SUS SUS SUS SUS SUS IFC*                                                                               SUS IFC*                                       color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color   color                   Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Gas          N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                       introduced                                                                     Gas · pressure                                                                     5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1250                                                                               1350                                                                               1000                                                                               1250                                                                               1350                                                                               1000                                                                               1400                                                                               900 1400                                                                               900                           (HV)                                                                           Tone         Gold                                                                               Deep                                                                               Light                                                                              Gold                                                                               Deep                                                                               Light                                                                              Gold                                                                               IFC*                                                                               Gold                                                                               IFC*                                           gold                                                                               gold    gold                                                                               gold                                          Total film thickness                                                                        1.4 3.0 0.4 1.4 3.0 0.4 3.4 0.3 3.4 0.3                 Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                                                                            .circleincircle                                                                .                             Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ             __________________________________________________________________________      *IFC: Generation of an interference color                                

                                      TABLE 2                                      __________________________________________________________________________               Example and  Invention               Comparison                                Comparative Example No.                                                                     7   8   9   10  11  12  5   6   7   8                   __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 2      FIG. 1  FIG. 2                            Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              SUS Brass                         material     304         304         304     304                               Undercoat    No  Yes Yes No  Yes Yes No  Yes No  Yes                           plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Gas          N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                       introduced                                                                     Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1250                                                                               1350                                                                               1000                                                                               1250                                                                               1350                                                                               1000                                                                               1400                                                                               900 1400                                                                               900                           (Hv)                                                                           Tone         Gold                                                                               Deep                                                                               Light                                                                              Gold                                                                               Deep                                                                               Light                                                                              Gold                                                                               IFC*                                                                               Gold                                                                               IFC*                                           gold                                                                               gold    gold                                                                               gold                                Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1                           N.sub.2 :C.sub.2 H.sub.2                                                       Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1200                                                                               1400                                                                               1000                                                                               1200                                                                               1400                                                                               1000                                                                               1450                                                                               900 1450                                                                               900                           (HV)                                                                           Tone         SUS SUS SUS SUS SUS SUS SUS IFC*                                                                               SUS IFC*                                       color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color   color                             Total film thickness                                                                        1.4 3.0 0.4 1.4 3.0 0.4 3.4 0.3 3.4 0.3                 Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                                                                            .circleincircle                                                                .                             Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ             __________________________________________________________________________      *IFC: Generation of an interference color                                

                                      TABLE 3                                      __________________________________________________________________________               Example and  Invention               Comparison                                Comparative Example No.                                                                     13  14  15  16  17  18  9   10  11  12                  __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 2      FIG. 1  FIG. 2                            Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              SUS Brass                         material     304         304         304     304                               Undercoat    No  Yes Yes No  Yes Yes No  Yes No  Yes                           plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1                           N.sub. 2 :C.sub.2 H.sub.2                                                      Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1200                                                                               1400                                                                               1000                                                                               1200                                                                               1400                                                                               1000                                                                               1450                                                                               900 1450                                                                               900                           (HV)                                                                           Tone         SUS SUS SUS SUS SUS SUS SUS IFC*                                                                               SUS IFC*                                       color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color   color                   Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     1:5 1:5 1:5 1:5 1:5 1:5 1:5 1:5 1:5 1:5                           N.sub.2 :C.sub.2 H.sub.2                                                       Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1200                                                                               1300                                                                               1000                                                                               1200                                                                               1300                                                                               1000                                                                               1350                                                                               900 1350                                                                               900                           (HV)                                                                           Tone         Dark                                                                               Gray                                                                               Light                                                                              Dark                                                                               Gray                                                                               Light                                                                              Dark                                                                               IFC*                                                                               Dark                                                                               IFC*                                       gray                                                                               black                                                                              gray                                                                               gray                                                                               black                                                                              gray                                                                               gray    gray                              Total film thickness                                                                        1.4 3.0 0.4 1.4 3.0 0.4 3.4 0.3 3.4 0.3                 Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                                                                            .circleincircle                                                                .                             Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ             __________________________________________________________________________      *IFC: Generation of an interference color                                

                                      TABLE 4                                      __________________________________________________________________________               Example and  Invention               Comparison                                Comparative Example No.                                                                     19  20  21  22  23  24  13  14  15  16                  __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 2      FIG. 1  FIG. 2                            Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              SUS Brass                         material     304         304         304     304                               Undercoat    No  Yes Yes No  Yes Yes No  Yes No  Yes                           plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     1:5 1:5 1:5 1:5 1:5 1:5 1:5 1:5 1:5 1:5                           N.sub. 2 :C.sub.2 H.sub.2                                                      Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1200                                                                               1300                                                                               1000                                                                               1200                                                                               1300                                                                               1000                                                                               1350                                                                               900 1350                                                                               900                           (HV)                                                                           Tone         Dark                                                                               Gray                                                                               Light                                                                              Dark                                                                               Gray                                                                               Light                                                                              Dark                                                                               IFC*                                                                               Dark                                                                               IFC*                                       gray                                                                               black                                                                              gray                                                                               gray                                                                               black                                                                              gray                                                                               gray    gray                    Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1                           N.sub.2 :C.sub.2 H.sub.2                                                       Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1200                                                                               1400                                                                               1000                                                                               1200                                                                               1400                                                                               1000                                                                               1450                                                                               900 1450                                                                               900                           (HV)                                                                           Tone         SUS SUS SUS SUS SUS SUS SUS IFC*                                                                               SUS IFC*                                       color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color   color                             Total film thickness                                                                        1.4 3.0 0.4 1.4 3.0 0.4 3.4 0.3 3.4 0.3                 Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                                                                            .circleincircle                                                                .                             Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ             __________________________________________________________________________      *IFC: Generation of an interference color                                

                                      TABLE 5                                      __________________________________________________________________________               Example and  Invention               Comparison                                Comparative Example No.                                                                     25  26  27  28  29  30  17  18  19  20                  __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 2      FIG. 1  FIG. 2                            Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              SUS Brass                         material     304         304         304     304                               Undercoat    No  Yes Yes No  Yes Yes No  Yes No  Yes                           plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1                           N.sub. 2 :C.sub.2 H.sub.2                                                      Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1200                                                                               1400                                                                               1000                                                                               1200                                                                               1400                                                                               1000                                                                               1450                                                                               900 1450                                                                               900                           (HV)                                                                           Tone         SUS SUS SUS SUS SUS SUS SUS IFC*                                                                               SUS IFC*                                       color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color   color                   Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     3:1 3:1 3:1 3:1 3:1 3:1 3:1 3:1 3:1 3:1                           N.sub.2 :C.sub.2 H.sub.2                                                       Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1350                                                                               1450                                                                               1100                                                                               1350                                                                               1450                                                                               1100                                                                               1500                                                                               900 1500                                                                               900                           (HV)                                                                           Tone         Brown                                                                              Dark                                                                               Light                                                                              Brown                                                                              Dark                                                                               Light                                                                              Brown                                                                              IFC*                                                                               Brown                                                                              IFC*                                           brown                                                                              brown   brown                                                                              brown                                         Total film thickness                                                                        1.4 3.0 0.4 1.4 3.0 0.4 3.4 0.3 3.4 0.3                 Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                                                                            .circleincircle                                                                .                             Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ             __________________________________________________________________________      *IFC: Generation of an interference color                                

                                      TABLE 6                                      __________________________________________________________________________               Example and  Invention               Comparison                                Comparative Example No.                                                                     31  32  33  34  35  36  21  22  23  24                  __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 2      FIG. 1  FIG. 2                            Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              SUS Brass                         material     304         304         304     304                               Undercoat    No  Yes Yes No  Yes Yes No  Yes No  Yes                           plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     3:1 3:1 3:1 3:1 3:1 3:1 3:1 3:1 3:1 3:1                           N.sub. 2 :C.sub.2 H.sub.2                                                      Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1350                                                                               1450                                                                               1100                                                                               1350                                                                               1450                                                                               1100                                                                               1500                                                                               900 1500                                                                               900                           (HV)                                                                           Tone         Brown                                                                              Dark                                                                               Light                                                                              Brown                                                                              Dark                                                                               Light                                                                              Brown                                                                              IFC*                                                                               Brown                                                                              IFC*                                           brown                                                                              brown   brown                                                                              brown                               Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1                           N.sub.2 :C.sub.2 H.sub.2                                                       Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1200                                                                               1400                                                                               1000                                                                               1200                                                                               1400                                                                               1000                                                                               1450                                                                               900 1450                                                                               900                           (HV)                                                                           Tone         SUS SUS SUS SUS SUS SUS SUS IFC*                                                                               SUS IFC*                                       color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color   color                             Total film thickness                                                                        1.4 3.0 0.4 1.4 3.0 0.4 3.4 0.3 3.4 0.3                 Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                                                                            .circleincircle                                                                .                             Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ             __________________________________________________________________________      *IFC: Generation of an interference color                                

                                      TABLE 7                                      __________________________________________________________________________               Example and  Invention               Comparison                                Comparative Example No.                                                                     37  38  39  40  41  42  25  26  27  28                  __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 2      FIG. 1  FIG. 2                            Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              SUS Brass                         material     304         304         304     304                               Undercoat    No  Yes Yes No  Yes Yes No  Yes No  Yes                           plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1                           N.sub. 2 :C.sub.2 H.sub.2                                                      Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μ m)                                                                       Hardness     1200                                                                               1400                                                                               1000                                                                               1200                                                                               1400                                                                               1000                                                                               1450                                                                               900 1450                                                                               900                           (HV)                                                                           Tone         SUS SUS SUS SUS SUS SUS SUS IFC*                                                                               SUS IFC*                                       color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color   color                   Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Gas          O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                       introduced                                                                     Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1350                                                                               1450                                                                               1100                                                                               1350                                                                               1450                                                                               1100                                                                               1500                                                                               900 1500                                                                               900                           (HV)                                                                           Tone         Blue                                                                               Dark                                                                               Light                                                                              Blue                                                                               Dark                                                                               Light                                                                              Blue                                                                               IFC*                                                                               Blue                                                                               IFC*                                           blue                                                                               blue    blue                                                                               blue                                          Total film thickness                                                                        1.4 3.0 0.4 1.4 3.0 0.4 3.4 0.3 3.4 0.3                 Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                                                                            .circleincircle                                                                .                             Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ             __________________________________________________________________________      *IFC: Generation of an interference color                                

                                      TABLE 8                                      __________________________________________________________________________               Example and  Invention               Comparison                                Comparative Example No.                                                                     43  44  45  46  47  48  29  30  31  32                  __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 2      FIG. 1  FIG. 2                            Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              Zinc                                                                               SUS Brass                                                                              SUS Brass                         material     304         304         304     304                               Undercoat    No  Yes Yes No  Yes Yes No  Yes No  Yes                           plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti  Ti                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Gas          O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                       introduced                                                                     Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1350                                                                               1450                                                                               1100                                                                               1350                                                                               1450                                                                               1100                                                                               1500                                                                               900 1500                                                                               900                           (HV)                                                                           Tone         Blue                                                                               Dark                                                                               Light                                                                              Blue                                                                               Dark                                                                               Light                                                                              Blue                                                                               IFC*                                                                               Blue                                                                               IFC*                                           blue                                                                               blue    blue                                                                               blue                                Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr  Cr                            source                                                                         Processing   7   15  2   7   15  2   17  1.5 17  1.5                           time (min)                                                                     Ratio of     1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1 1:1                           N.sub.2 :C.sub.2 H.sub.2                                                       Gas pressure 5   9   2   5   9   2   5   9   5   9                             (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 0.7 1.5 0.2 1.7 0.15                                                                               1.7 0.15                          (μm)                                                                        Hardness     1200                                                                               1400                                                                               1000                                                                               1200                                                                               1400                                                                               1000                                                                               1450                                                                               900 1450                                                                               900                           (HV)                                                                           Tone         SUS SUS SUS SUS SUS SUS SUS IFC*                                                                               SUS IFC*                                       color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color                                                                              color   color                             Total film thickness                                                                        1.4 3.0 0.4 1.4 3.0 0.4 3.4 0.3 3.4 0.3                 Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                                                                            .circleincircle                                                                .                             Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ                       Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   .circleincircle                                                                .                             Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                                                   Δ             __________________________________________________________________________      *IFC: Generation of an interference color                                

                                      TABLE 9                                      __________________________________________________________________________               Example and  Invention   Comparison                                            Comparative Example No.                                                                     49  50  51  33  34                                      __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 1                                                Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                             material     304         304                                                   Undercoat    No  Yes Yes No  Yes                                               plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Pure                                                                               Pure                                                                               Pure                                                                               Pure                                                                               Pure                                              source       Ti  Ti  Ti  Ti  Ti                                                Processing   7   15  2   17  1.5                                               time (min)                                                                     Gas          N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                           introduced                                                                     Gas pressure 5   9   2   5   9                                                 (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 1.7 0.15                                              (μm)                                                                        Hardness     1250                                                                               1350                                                                               1000                                                                               1400                                                                               900                                               (HV)                                                                           Tone         Gold                                                                               Deep                                                                               Light                                                                              Gold                                                                               IFC*                                                               gold                                                                               gold                                            Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Pure                                                                               Pure                                                                               Pure                                                                               Pure                                                                               Pure                                              source       Ti  Ti  Ti  Ti  Ti                                                Processing   7   15  2   17  1.5                                               time (min)                                                                     Gas          O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                           introduced                                                                     Gas pressure 5   9   2   5   9                                                 (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 1.7 0.15                                              (μm)                                                                        Hardness     1350                                                                               1450                                                                               1100                                                                               1500                                                                               900                                               (HV)                                                                           Tone         Blue                                                                               Dark                                                                               Light                                                                              Blue                                                                               IFC*                                                               blue                                                                               blue                                                      Total film thickness                                                                        1.4 3.0 0.4 3.4 0.3                                     Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                           Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                  Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                           Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                  sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                  Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                 __________________________________________________________________________      *IFC: Interference color                                                 

                                      TABLE 10                                     __________________________________________________________________________               Example and  Invention   Comparison                                            Comparative Example No.                                                                     52  53  54  35  36                                      __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 1                                                Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                             material     304         304                                                   Undercoat    No  Yes Yes No  Yes                                               plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Pure                                                                               Pure                                                                               Pure                                                                               Pure                                                                               Pure                                              source       Ti  Ti  Ti  Ti  Ti                                                Processing   7   15  2   17  1.5                                               time (min)                                                                     Gas          O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                                                            O.sub.2                                           introduced                                                                     Gas pressure 5   9   2   5   9                                                 (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 1.7 0.1                                               (μm)                                                                        Hardness     1350                                                                               1450                                                                               1100                                                                               1500                                                                               900                                               (HV)                                                                           Tone         Blue                                                                               Dark                                                                               Light                                                                              Blue                                                                               IFC*                                                               blue                                                                               blue                                            Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Pure                                                                               Pure                                                                               Pure                                                                               Pure                                                                               Pure                                              source       Ti  Ti  Ti  Ti  Ti                                                Processing   7   15  2   17  1.5                                               time (min)                                                                     Gas          N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                           introduced                                                                     Gas pressure 5   9   2   5   9                                                 (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 1.7 0.1                                               (μm)                                                                        Hardness     1250                                                                               1350                                                                               1000                                                                               1400                                                                               900                                               (HV)                                                                           Tone         Gold                                                                               Deep                                                                               Light                                                                              Gold                                                                               IFC*                                                               gold                                                                               gold                                                      Total film thickness                                                                        1.4 3.0 0.4 3.4 0.3                                     Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                           Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                  Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                           Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                  sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                  Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                 __________________________________________________________________________      *IFC: Interference color                                                 

                                      TABLE 11                                     __________________________________________________________________________               Example and  Invention   Comparison                                            Comparative Example No.                                                                     55  56  57  37  38                                      __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 1                                                Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                             material     304         304                                                   Undercoat    No  Yes Yes No  Yes                                               plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Pure                                                                               Pure                                                                               Pure                                                                               Pure                                                                               Pure                                              source       Ti  Ti  Ti  Ti  Ti                                                Processing   7   15  2   17  1.5                                               time (min)                                                                     Gas          N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                           introduced                                                                     Gas pressure 5   9   2   5   9                                                 (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 1.7 0.15                                              (μm)                                                                        Hardness     1250                                                                               1350                                                                               1000                                                                               1400                                                                               900                                               (HV)                                                                           Tone         Gold                                                                               Deep                                                                               Light                                                                              Gold                                                                               IFC*                                                               gold                                                                               gold                                            Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Pure                                                                               Pure                                                                               Pure                                                                               Pure                                                                               Pure                                              source       Ti  Ti  Ti  Ti  Ti                                                Processing   7   15  2   17  1.5                                               time (min)                                                                     Ratio of     3:1 3:1 3:1 3:1 3:1                                               O.sub.2 :C.sub.2 H.sub.2                                                       Gas pressure 5   9   2   5   9                                                 (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 1.7 0.15                                              (μm)                                                                        Hardness     1350                                                                               1450                                                                               1100                                                                               1500                                                                               900                                               (HV)                                                                           Tone         Brown                                                                              Dark                                                                               Light                                                                              Brown                                                                              IFC*                                                               brown                                                                              brown                                                     Total film thickness                                                                        1.4 3.0 0.4 3.4 0.3                                     Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                           Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                  Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                           Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                  sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                  Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                 __________________________________________________________________________      *IFC: Interference color                                                 

                                      TABLE 12                                     __________________________________________________________________________               Example and  Invention   Comparison                                            Comparative Example No.                                                                     58  59  60  39  40                                      __________________________________________________________________________               Method shown in                                                                             FIG. 1      FIG. 1                                                Substrate    SUS Brass                                                                              Zinc                                                                               SUS Brass                                             material     304         304                                                   Undercoat    No  Yes Yes No  Yes                                               plating                                                              Hard film for 1st                                                                        Producing conditions                                                 layer     Evaporation  Pure                                                                               Pure                                                                               Pure                                                                               Pure                                                                               Pure                                              source       Ti  Ti  Ti  Ti  Ti                                                Processing   7   15  2   17  1.5                                               time (min)                                                                     Ratio of     3:1 3:1 3:1 3:1 3:1                                               O.sub.2 :C.sub.2 H.sub.2                                                       Gas pressure 5   9   2   5   9                                                 (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 1.7 0.15                                              (μm)                                                                        Hardness     1350                                                                               1450                                                                               1100                                                                               1500                                                                               900                                               (HV)                                                                           Tone         Brown                                                                              Dark                                                                               Light                                                                              Brown                                                                              IFC*                                                               brown                                                                              brown                                           Hard film for 2nd                                                                        Producing conditions                                                 layer     Evaporation  Pure                                                                               Pure                                                                               Pure                                                                               Pure                                                                               Pure                                              source       Ti  Ti  Ti  Ti  Ti                                                Processing   7   15  2   17  1.5                                               time (min)                                                                     Gas          N.sub.2                                                                            N.sub. 2                                                                           N.sub.2                                                                            N.sub.2                                                                            N.sub.2                                           introduced                                                                     Gas pressure 5   9   2   5   9                                                 (× 10.sup.-4 Torr)                                                       Film                                                                           characteristics                                                                Thickness    0.7 1.5 0.2 1.7 0.15                                              (μm)                                                                        Hardness     1250                                                                               1350                                                                               1000                                                                               1400                                                                               900                                               (HV)                                                                           Tone         Gold                                                                               Deep                                                                               Light                                                                              Gold                                                                               IFC*                                                               gold                                                                               gold                                                      Total film thickness                                                                        1.4 3.0 0.4 3.4 0.3                                     Evaluation                                                                               Tone         ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                           Adherence    ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                                                            ⊚                                  Wear resistance                                                                             ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                           Corrosion resistance                                                           Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                  sweat                                                                          Artificial   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                                                   ⊚                                  Sea water                                                                      Hardness     ⊚                                                                   ⊚                                                                   ○                                                                           ⊚                                                                   Δ                                 __________________________________________________________________________      *IFC: Interference color                                                 

                  TABLE 13                                                         ______________________________________                                                          Condition                                                             Trade name Drying      Removing                                        ______________________________________                                         Organic   SPR-557W     Natural     Trichlene                                   coating   (Sanei Kagaku                                                                               drying      ultrasonic                                            K.K.)        30 to 60 min                                                                               cleaning                                                           Hot-air                                                                        drying 150° C.                                                          30 min                                                  Inorganic Heat-resistant                                                                              Natural     Trichlene                                   coating   masking      drying      ultrasonic                                            material-D   30 to 60 min                                                                               cleaning                                              (Okuno Seiyaku                                                                              Hot-air                                                           K.K.)        drying 200° C.                                                          60 min                                                  ______________________________________                                    

                  TABLE 14                                                         ______________________________________                                                    Condition                                                                        Composition of                                                    Hard film    remover       Method                                              ______________________________________                                         Ti hard film 47% HF    1 vol   Temp.: normal                                                61% HNO.sub.3                                                                            1 vol   temperature                                                                    Immersing time:                                                                10 min.                                         Cr hard film not less than Temp.: normal                                                    90% H.sub.3 PO.sub.4                                                                         temperature                                                                    Anodic                                                                         electrolysis:                                                                  5V × 5 min                                    ______________________________________                                    

                                      TABLE 15                                     __________________________________________________________________________            FIG. No.                Structure and thickness                         Sample 3 4 5 6 7 8 9 10                                                                               11                                                                               12                                                                               13                                                                               14                                                                               of undercoat plating                            __________________________________________________________________________     Example No.                                                                           2  8                                                                               14                                                                               20                                                                               26                                                                               32                                                                               38                                                                               44                                                                               50                                                                               53                                                                               56                                                                               59                                                                                Cu(4 μm) + Ni(4 μm) + 80 wt %                                           Pd--Ni (3 μm)                                       5 11                                                                               17                                                                               23                                                                               29                                                                               35                                                                               41                                                                               47         Cu(4 μm) + Ni(4 μm) + 80 wt %                                           Pd--Ni (3 μm)                                       3  9                                                                               15                                                                               21                                                                               27                                                                               33                                                                               39                                                                               45                                                                               51                                                                               54                                                                               57                                                                               60                                                                               Cu(15 μm) + Ni(10 μm) + 80 wt %                                          Pd--Ni (3 μm)                                       6 12                                                                               18                                                                               24                                                                               30                                                                               36                                                                               42                                                                               48        Cu(15 μm) + Ni(10 μm) + 80 wt %                                          Pd--Ni (3 μm)                                Comparative                                                                           2  6                                                                               10                                                                               14                                                                               18                                                                               22                                                                               26                                                                               30                                                                               34                                                                               36                                                                               38                                                                               40                                                                                Cu(4 μm) + Ni(4 μm) + 80 wt %                                           Pd--Ni (3 μm)                                Example No.                                                                           4  8                                                                               12                                                                               16                                                                               20                                                                               24                                                                               28                                                                               32        Cu(15 μm) + Ni(10 μm) + 80 wt %                                          Pd--Ni (3 μm)                                __________________________________________________________________________

Criteria of properties evaluated in Tables 1 to 12 are shown in Table 16.

                                      TABLE 16                                     __________________________________________________________________________     Properties    Wear          Corrosion                                                                             Hardness                                    Mark  Tone    resistance                                                                            Adherence                                                                             resistance                                                                            (HV)                                        __________________________________________________________________________     ⊚                                                                     Intended                                                                               Not worn                                                                              No separation                                                                         No corrosion                                                                          Not less than 1200                                tone                                                                     ○                                                                             Substantially                                                                          Little worn                                                                           Almost no                                                                             Almost no                                                                             Less than 1200 to                                 intended tone                                                                          No exposure                                                                           separation                                                                            corrosion                                                                             not less than 1000                          Δ                                                                              Slight devia-                                                                          Partial                                                                               Slight or                                                                             Slight or                                                                             Less than 1000 to                                 tion from                                                                              exposure of                                                                           partial                                                                               partial                                                                               not less than 900                                 intended tone                                                                          material                                                                              separation                                                                            corrosion                                          ×                                                                              Considerable                                                                           Exposure of                                                                           Separation                                                                            Corrosion                                                                             Less than 900                                     deviation from                                                                         material                                                                              over the                                                                              over the                                                 intended tone                                                                          over the                                                                              entire or                                                                             entire or                                                        entire considerable                                                                          considerable                                                     surface                                                                               portion                                                                               portion                                            __________________________________________________________________________

The thicknesses of the ion-plated films were determined using x-ray analysis. The tone visibly was judged and hardness was measured by a micro Vickers hardness testing machine with a load of 10 g. In order to examine wear resistance, the side surface of a watch case was reciprocated 30,000 times, at a stroke of 10 cm, while applying a load of 500 g to the watch case in close contact with cow leather. The degree of wear of the side surface of watch case was observed and recorded.

A compression load was applied to the watch case from both ends by a vice to bend an ornamental member in the shape of a watch exterior member. The bent portion had an angle of not less than 90°, and the degree of separation of the hard film at the bent portion was examined to determine adherence. To measure resistance to corrosion the ornamental member was immersed in artificial sweat and artificial sea water (3% NaCl) for twenty hours at a temperature of 40° C. and a humidity of 90%. Corrosion and color change were examined.

In Examples 1-60 showing ornamental members prepared in accordance with the invention, each ornamental member including a Cr hard film and a Ti hard film included two color tones having high ornamental value. No corrosion was observed in the corrosion resistance tests using artificial sweat and artificial sea water.

In the adherence test, the adherence was sufficient for an exterior member of a watch in each of Examples 1-60. When the thickness of a single layer of a hard film exceeded 1.5 μm and the total film thickness exceeded 3.0 μm, as in Comparative Examples 1, 3, 5, 7, 9, 11, 13, 15, 17, 19, 21, 23, 25, 27, 29, 31, 33, 35, 37 and 39, the adherence was reduced and partial separation between the hard films was observed. Thus, a single layer of hard film is preferably not more than about 1.5 μm to obtain sufficient adherence.

On the other hand, when the thickness of single layer or a hard film was less than 0.2 μm, as in Comparative Examples 2, 4, 6, 8, 10, 12, 14, 16, 18, 20, 22, 24, 26, 28, 30, 32, 34, 36, 38 and 40, an interference color, color shading or partial color change occurred, and it was impossible to achieve external tone stability. In addition, it was not possible to obtain the necessary wear resistance from a hard film less than about 0.2 μm since such a thin film does not have a hardness of 1000 Hv. Thus, the thickness of a single layer of hard film is between about 0.2 and 1.5 μm and preferably between about 0.2 and 0.8 μm to obtain sufficient adherence, tone stability and wear resistance.

When the surface of an ornamental member prepared in accordance with the invention is subject to various treatments, such as stripe patterning, check patterning, pear-skin patterning and mirror polishing, and hard films are formed thereon in accordance with the invention, the exterior can also present the same ornamentality of the surface treatment as the surface with no hard films formed thereon. If a hard film is further subjected to polishing by a polishing disk or the like, it is possible to produce lustrous exterior with high ornamentality. The surface of the polished hard film has a hardness of not less than 1000 Hv, and no exposure of the material was observed in wear resistance test.

In Examples 1-60, the general tendency was that the tone became darker with an increase in gas pressure, while the tone became lighter with a drop in gas pressure. However, the variation was small enough to judge the tones as identical in external appearance. Thus, the ornamental members prepared in accordance with the invention can be used as an exterior member for all parts or specifics parts of a watch.

Ion plating was carried out under constant conditions to control and maintain a constant tone of the hard film in Examples 1-60 set forth in Tables 1-12. Thus, the type of reaction gas, gas flow ratio, the gas pressure, the amount of evaporation of Ti or Cr and the processing time were kept constant. When ten samples formed separately from each other under the same conditions were compared visually and by color-difference meter, no difference was observed. Thus, the method of forming an ornamental member in accordance with the invention has high repetitional precision.

In another embodiment of the invention, a multi-colored ornamental member includes three or more color tones on a substrate as illustrated in FIGS. 15-21. A Cr or Ti hard film 12 of a color A, a Cr or Ti hard film 13 of a color B, a Cr or Ti hard film 14 of a color C and a Cr or Ti hard film 15 of a color D are laminated on substrate 1.

In particular, hard film 12 may be a Ti hard film, hard film 13 may be a Ti hard film of a different color than that of hard film 12, hard film 14 may be a Cr hard film and hard film 15 may be a Ti hard film of a different color than that of hard films 12 and 13.

A gold colored hard film may be formed of a material including Ti and N, a dark grey hard film may be formed of a material including Ti, N and C, a blue hard film may be formed of a material including Ti and O and a brown colored hard film may be formed of a compound including Ti, C and O. A stainless steel colored hard film may be formed of a material including Cr, N and C. Each of the hard films described above may be used to form the multi-colored ornamental member in accordance with the invention. Appropriate combinations of the second-layer ion plating method shown in FIG. 1 and the second-layer etching method shown in FIG. 2 easily produce ornamental members including three visible color tones under the same conditions as those described in Tables 1-12. Corrosion resistance, wear resistance, color tone and adherence are all satisfactory.

In the embodiments depicted in FIGS. 18, 19 and 21, when the total thickness of the three hard films exceeded about 3.0 μm, the adherence of the three layered portion was lowered in the same manner as in Comparative Examples 1, 3, 5, 7, 9, 11, 13, 15, 17, 19, 21, 23, 25, 27, 29, 31, 33, 35, 37, and 39. Thus, the thickness of each hard film is between about 0.2 and 1.5 μm. Preferably, the thickness of each hard layer is between about 0.2 and 0.8 μm.

The method for forming an ornamental member in accordance with the invention is not limited to exterior members of watches. Ornaments and accessories, including frames for glasses, lighter cases, ornamental bands, buckles, tiepins, rings and utensils, may be formed by the above-described method. In sum, an ornamental member in accordance with the invention includes at least two hard films of different colors to create a multi-colored exterior surface. The hard films have a hardness of not less than about 1000 Hv and include a stainless steel colored film, a gold colored film, a dark grey film, a blue film and a brown film.

High ornamental and functional value is obtained by a combination of hard films of at least two colors, including gold and brown, gold and blue, stainless steel and gold, stainless steel and dark grey, and stainless steel and brown. The adherence of the hard layers to the substrate and to each other, and the scratch resistance, the wear resistance and the corrosion resistance are superior to those of a conventional ornamental member.

In a first method of forming an ornamental member in accordance with the invention, including one Cr hard film and one Ti hard film or two Ti hard film, a first hard film is ion plated on a substrate. A heat resistant masking material is deposited in a pattern on the first hard film and baked and a second hard film is ion plated on the first hard film and the masking material. The masking material is removed, removing the portion of the second hard film formed over it. It is possible to choose the structures of the hard films to reduce the masking area and the masking time, thus, reducing the cost.

In a second method for forming an ornamental member in accordance with the invention, including one Cr hard film and one Ti hard film, a first hard film is ion plated on a substrate. A second hard film is ion plated on the first hard film and the second hard film is partially removed by etching. However, when two Ti hard films of different colors are used as the first hard film and the second hard film, it is difficult to form an ornamental member in accordance with the invention using the second-layer etching method.

It will thus be seen that the objects set forth above, among those made apparent from the preceding description, are efficiently attained and, since certain changes may be made in carrying out the above method and in the article set forth without departing from the spirit and scope of the invention, it is intended that all matter contained in the above description and shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense.

It is also to be understood that the following claims are intended to cover all of the generic and specific features of the invention herein described and all statements of the scope of the invention which, as a matter of language, might be said to fall therebetween.

Particularly it is to be understood that in said claims, ingredients or compounds recited in the singular are intended to include compatible mixtures of such ingredients wherever the sense permits. 

What is claimed is:
 1. An ornamental member, comprising:a substrate; a first hard film having a hardness of at least about 1000 HV deposited on said substrate; and a second hard film having a hardness of at least about 1000 HV selectively deposited on said first hard film so that portions of the first hard film are exposed, said first hard film and said second hard film having different color tones, at least one of said first hard film and said second hard film is a Ti containing ceramic and the other of said first hard film and said second hard film is selected from the group consisting of a Cr containing ceramic.
 2. The ornamental member of claim 1, wherein said Cr containing ceramic film contains Cr, N and C.
 3. The ornamental member of claim 1, wherein said Ti to containing ceramic are selected from the group consisting of:a hard film containing Ti and N; a hard film containing Ti, N and C, a hard film containing Ti and O, and a hard film containing Ti, O and C.
 4. The ornamental member of claim 1, wherein said first hard film is between about 0.2 and 1.5 μm thick and said second hard film is between about 0.2 and 1.5 μm thick.
 5. The ornamental member of claim 4, wherein said first hard film is between about 0.2 and 0.8 μm thick and said second hard film is between about 0.2 and 0.8 μm thick.
 6. The ornamental memeber of claim 1, wherein said ornamental member presents two color tones and one of said color tones is the color of said first hard film and the other of said color tones is the color tone of said second hard film.
 7. The ornamental member of claim 1, further including a third hard film selectively deposited on said second hard film, said third hard film selected from the group consisting of a Cr containing film and a Ti containing ceramic film.
 8. The ornamental member of claim 7, wherein said first hard film is between about 0.2 and 1.0 μm thick, said second hard film is between about 0.2 and 1.0 μm thick and said third hard film is between about 0.2 and 1.0 μm thick.
 9. The ornamental member of claim 8, wherein said first hard film is between about 0.2 and 0.8 μm thick, said second hard film is between about 0.2 and 0.8 μm thick and said third hard film is between about 0.2 and 0.8 μm thick.
 10. The ornamental member of claim 1, further including a third hard film selectively deposited on said first hard film at a portion at which said second hard film is not deposited on said first hard film.
 11. The ornamental member of claim 10, wherein said first hard film is between about 0.2 and 1.5 μm thick, said second hard film is between about 0.2 and 1.5 μm thick, and said third hard film is between about 0.2 and 1.5 μm thick.
 12. The ornamental member of claim 11, wherein said first hard film is between about 0.2 and 0.8 μm thick, said second hard film is between about 0.2 and 0.8 μm thick and said third hard film is between about 0.2 and 0.8 μm thick.
 13. The ornamental member of claim 1, wherein said first hard film is said Cr containing ceramic film and said second hard film is said Ti containing ceramic film.
 14. The ornamental member of claim 1, wherein said first hard film is a Ti containing ceramic film and said second hard film is a Cr containing film.
 15. The ornamental member of claim 1, wherein said first hard film and said second hard film are Ti containing ceramic films.
 16. The ornamental member of claim 1, further including at least one layer of undercoat plating deposited on said substrate, said undercoat plating selected from the group consisting of gold, gold alloy, chromium, palladium, palladium alloy, rhodium and ruthenium and combinations thereof with said first hard film deposited on said undercoat plating.
 17. The ornamental member of claim 1, further including at least one layer of a pre-undercoat plating, deposited on the substrate selected from the group consisting of copper, Ni and Ni alloy, and at least one layer of undercoat plating deposited on said pre-undercoat plating, said undercoat plating selected from the group consisting of gold, gold alloy, chromium, palladium, palladium alloy, rhodium and ruthenium and combinations thereof with said first hard film deposited on said undercoat plating.
 18. The ornamental member of claim 1, wherein the substrate is selected from the group consisting of stainless steel, a ceramic material, a copper alloy, a hard Ni-base alloy, a Co-based alloy, zinc, a zinc alloy and a plastic material.
 19. The ornamental member of claim 1, wherein said substrate is SUS 304 stainless steel.
 20. The ornamental member of claim 1, wherein said substrate is zinc.
 21. The ornamental member of claim 1, wherein said substrate is brass. 